    Electrochemical and biological characterization of thin-film platinum-iridium alloy electrode coatings: a chronic in vivo study
    (IOP Publishing, 2020-05) Dalrymple, Ashley; Huynh, Mario; Nayagam, Bryony; Lee, Curtis; Weiland, Greg; Petrossians, Artin; Whalen, John; Fallon, James; Shepherd, Robert
    OBJECTIVE: To evaluate the electrochemical properties, biological response, and surface characterization of an electrodeposited Platinum-Iridium (Pt-Ir) electrode coating on cochlear implants subjected to chronic stimulation in vivo. APPROACH: Electrochemical impedance spectroscopy (EIS), charge storage capacity (CSC), charge injection limit (CIL), and voltage transient (VT) impedance were measured bench-top before and after implant and in vivo. Coated Pt-Ir and uncoated Pt electrode arrays were implanted into cochlea of normal hearing rats and stimulated for ~4 hours/day, 5 days/week for 5 weeks. Neural function was monitored using electrically-evoked auditory brainstem responses. After explant, the electrode surfaces were assessed, and cochleae examined histologically. MAIN RESULTS: When measured on bench-top before and after stimulation, Pt-Ir coated electrodes had significantly lower VT impedance (p < 0.001) and significantly higher CSC (p < 0.001) and CIL (p < 0.001) compared to uncoated Pt electrodes. In vivo, the CSC and CIL of Pt-Ir were significantly higher than Pt throughout the implantation period (p = 0.047 and p < 0.001, respectively); however, the VT impedance (p = 0.3) was not. There was no difference in foreign body response between material cohorts, although cochleae implanted with coated electrodes contained small deposits of Pt-Ir. There was no evidence of increased neural loss or loss of neural function in either group. Surface examination revealed no Pt corrosion on any electrodes. SIGNIFICANCE: Electrodeposited Pt-Ir electrodes demonstrated significant improvements in electrochemical performance on the bench-top and in vivo compared to uncoated Pt. Neural function and tissue response to Pt-Ir electrodes were not different from uncoated Pt, despite small deposits of Pt-Ir in the tissue capsule. Electrodeposited Pt-Ir coatings offer promise as an improved electrode coating for active neural prostheses.
  • Thumbnail Image
    Item
    Electrochemical and biological performance of chronically stimulated conductive hydrogel electrodes
    (IOP Publishing, 2020-03) Dalrymple, Ashley; Robles, Ulises; Huynh, Mario; Nayagam, Bryony; Green, Rylie; Poole-Warren, Laura; Fallon, James; Shepherd, Robert
    OBJECTIVE: Evaluate electrochemical properties, biological response, and surface characterization of a conductive hydrogel (CH) coating following chronic in vivo stimulation. APPROACH: Coated CH or uncoated smooth platinum (Pt) electrode arrays were implanted into the cochlea of rats and stimulated over a 5 week period with more than 57 million biphasic current pulses. Electrochemical impedance spectroscopy (EIS), charge storage capacity (CSC), charge injection limit (CIL), and voltage transient (VT) impedance were measured on the bench before and after stimulation, and in vivo during the stimulation program. Electrically-evoked auditory brainstem responses were recorded to monitor neural function. Following explant, the cochleae were examined histologically and electrodes were examined using scanning electron microscopy. MAIN RESULTS: CH coated electrodes demonstrated a bench-top electrochemical advantage over Pt electrodes before and after the electrical stimulation program. In vivo, CH coated electrodes also had a significant advantage over Pt electrodes throughout the stimulation program, exhibiting higher CSC (p = 0.002), larger CIL (p = 0.002), and lower VT impedance (p < 0.001). The CH cohort exhibited a greater tissue response (p = 0.003) with small deposits of particulate material within the tissue capsule. There was no loss in auditory neuron density or change in neural response thresholds in any cochleae. SEM examination of the electrode surface revealed that most CH electrodes exhibited some coating loss; however, there was no evidence of corrosion in the underlying Pt. SIGNIFICANCE: CH coated electrodes demonstrated significant electrochemical advantages on the bench-top and in vivo and maintained neural function despite an increased tissue response and coating loss. While further research is required to understand the cause of the coating loss, CH electrodes provide promise for use in neural prostheses.
  • Thumbnail Image
    Item
    Electrochemical and mechanical performance of reduced graphene oxide, conductive hydrogel, and electrodeposited Pt-Ir coated electrodes: an active in vitro study
    (IOP Publishing, 2019-10) Dalrymple, Ashley; Huynh, Mario; Robles, Ulyises; Marroquin, Jason; Lee, Curtis; Petrossians, Artin; Whalen, John; Li, Dan; Parkington, Helena; Forsythe, John; Green, Rylie; Poole-Warren, Laura; Shepherd, Robert; Fallon, James
    OBJECTIVE: To systematically compare the in vitro electrochemical and mechanical properties of several electrode coatings that have been reported to increase the efficacy of medical bionics devices by increasing the amount of charge that can be delivered safely to the target neural tissue. APPROACH: Smooth platinum (Pt) ring and disc electrodes were coated with reduced graphene oxide, conductive hydrogel, or electrodeposited Pt-Ir. Electrodes with coatings were compared with uncoated smooth Pt electrodes before and after an in vitro accelerated aging protocol. The various coatings were compared mechanically using the adhesion-by-tape test. Electrodes were stimulated in saline for 24 hours/day 7 days/week for 21 days at 85 masculineC (1.6-year equivalence) at a constant charge density of 200 muC/cm2/phase. Electrodes were graded on surface corrosion and trace analysis of Pt in the electrolyte after aging. Electrochemical measurements performed before, during, and after aging included electrochemical impedance spectroscopy, cyclic voltammetry, and charge injection limit and impedance from voltage transient recordings. MAIN RESULTS: All three coatings adhered well to smooth Pt and exhibited electrochemical advantage over smooth Pt electrodes prior to aging. After aging, graphene coated electrodes displayed a stimulation-induced increase in impedance and reduction in the charge injection limit (p < 0.001), alongside extensive corrosion and release of Pt into the electrolyte. In contrast, both conductive hydrogel and Pt-Ir coated electrodes had smaller impedances and larger charge injection limits than smooth Pt electrodes (p < 0.001) following aging regardless of the stimulus level and with little evidence of corrosion or Pt dissolution. SIGNIFICANCE: This study rigorously tested the mechanical and electrochemical performance of electrode coatings in vitro and provided suitable candidates for future in vivo testing.
  • Thumbnail Image
    Item
    Platinum dissolution and tissue response following long-term electrical stimulation at high charge densities
    (IOP Publishing, 2021-02) Shepherd, Robert; Carter, Paul; Dalrymple, Ashley; Enke, Ya Lang; Wise, Andrew; Nguyen, Trung; Firth, James; Thompson, Alex; Fallon, James
    OBJECTIVE: Established guidelines for safe levels of electrical stimulation for neural prostheses are based on a limited range of the stimulus parameters used clinically. Recent studies have reported particulate platinum (Pt) associated with long-term clinical use of these devices, highlighting the need for more carefully defined safety limits. We previously reported no adverse effects of Pt corrosion products in the cochleae of guinea pigs following 4 weeks of electrical stimulation using charge densities far greater than the published safe limits for cochlear implants. The present study examines the histopathological effects of Pt within the cochlea following continuous stimulation at a charge density well above the defined safe limits for periods up to 6 months. APPROACH: Six cats were bilaterally implanted with Pt electrode arrays and unilaterally stimulated using charge balanced current pulses at a charge density of 267 C/cm2/phase using a tripolar electrode configuration. Electrochemical measurements were made throughout the implant duration and evoked potentials recorded at the outset and on completion of the stimulation program. Cochleae were examined histologically for particulate Pt, tissue response, and auditory nerve survival; electrodes were examined for surface corrosion; and cochlea, brain, kidney, and liver tissue analysed for trace levels of Pt. MAIN RESULTS: Chronic stimulation resulted in both a significant increase in tissue response and particulate Pt within the tissue capsule surrounding the electrode array compared with implanted, unstimulated control cochleae. Importantly, there was no stimulus-induced loss of auditory neurons or increase in evoked potential thresholds. Stimulated electrodes were significantly more corroded compared with unstimulated electrodes. Trace analysis revealed Pt in both stimulated and control cochleae although significantly greater levels were detected within stimulated cochleae. There was no evidence of Pt in brain or liver; however, trace levels of Pt were recorded in the kidneys of two animals. Finally, increased charge storage capacity and charge injection limit reflected the more extensive electrode corrosion associated with stimulated electrodes. SIGNIFICANCE: Long-term electrical stimulation of Pt electrodes at a charge density well above existing safety limits and nearly an order of magnitude higher than levels used clinically, does not adversely affect the auditory neuron population or reduce neural function, despite a stimulus-induced tissue response and the accumulation of Pt corrosion product. The mechanism resulting in Pt within the unstimulated cochlea is unclear, while the level of Pt observed systemically following stimulation at these very high charge densities does not appear to be of clinical significance.
  • Thumbnail Image
    Item
    Shepherd, R. K., P. Carter, Y. L. Enke, A. Thompson, B. Flynn, E. Trang, A. Dalrymple, and J. B. Fallon. 2020. Chronic intracochlear electrical stimulation at high charge densities: Reducing platinum dissolution
    (IOP Publishing, 2020-09) Shepherd, Robert; Carter, Paul; Enke, Ya Lang; Thompson, Alex; Flynn, Brianna; Trang, Ella; Dalrymple, Ashley; Fallon, James
    OBJECTIVE: Cochleae of long-term cochlear implant users have shown evidence of particulate platinum (Pt) corroded from the surface of Pt electrodes. The pathophysiological effect of Pt within the cochlea has not been extensively investigated. We previously evaluated the effects of Pt corrosion at high charge densities and reported negligible pathophysiological impact. The present study extends this work by examining techniques that may reduce Pt corrosion. APPROACH: Deafened guinea pigs were continuously stimulated for 28 days using biphasic current pulses at extreme charge densities using: (i) electrode shorting; (ii) electrode shorting with capacitive coupling (CC); or (iii) electrode shorting with alternating leading phase (AP). On completion of stimulation, cochleae were examined for corrosion product, tissue response, auditory nerve (AN) survival and trace levels of Pt; and electrodes examined for surface corrosion. MAIN RESULTS: Pt corrosion was evident at > 200 μC/cm2/phase; the amount dependent on charge density (p < 0.01) and charge recovery technique (p < 0.01); reduced corrosion was apparent using CC. Tissue response increased with charge density (p < 0.007); cochleae stimulated at > 200 μC/cm2/phase exhibited a vigorous response including a focal region of necrosis and macrophages. Notably, tissue response was not dependent on the charge recovery technique (p = 0.56). Despite stimulation at high charge densities resulting in significant levels of Pt corrosion, there was no stimulus induced loss of ANs. SIGNIFICANCE: Significant increases in tissue response and Pt corrosion were observed following stimulation at high charge densities. Charge recovery using CC, and to a lesser extent AP, reduced the amount of Pt corrosion but not the tissue response. Stimulation at change densities an order of magnitude higher than those used when programming cochlear implant recipients in the clinic, produced a vigorous tissue response and corrosion products without evidence of neural loss.